Differences in birch tar composition are explained by adhesive function in the central European Iron Age.

Birch bark tar is the most widely documented adhesive in prehistoric Europe. More recent periods attest to a diversification in terms of the materials used as adhesives and their application. Some studies have shown that conifer resins and beeswax were added to produce compound adhesives. For the Iron Age, no comparative large-scale studies have been conducted to provide a wider perspective on adhesive technologies. To address this issue, we identify adhesive substances from the Iron Age in north-eastern France. We applied organic residue analysis to 65 samples from 16 archaeological sites. This included residues adhering to ceramics, from vessel surface coatings, repaired ceramics, vessel contents, and adhesive lumps. Our findings show that, even during the Iron Age in north-eastern France, birch bark tar is one of the best-preserved adhesive substances, used for at least 400 years. To a lesser extent, Pinaceae resin and beeswax were also identified. Through statistical analyses, we show that molecular composition differs in samples, correlating with adhesive function. This has implications for our understanding of birch bark tar production, processing and mode of use during the Iron Age in France and beyond.

pH-regulated Tannic acid and soybean protein isolate adhesive for enhanced performance in plant-based meat analogues.

A food adhesive comprising tannic acid (TA) and soybean protein isolate (SPI) was developed to establish a cohesive bond between soy protein gel and simulated fat. The impact of varying TA concentrations and pH levels on the adhesive's rheology, thermal stability, chemical structure, and tensile strength were investigated. Rheological results revealed a gradual decrease in adhesive viscosity with increasing TA content. Differential scanning calorimetry (DSC) and thermal gravimetric (TG) results indicated that the stability of the adhesive improved with higher TA concentrations, reaching its peak at 0.50% TA addition. The incorporation of TA resulted in the cross-linking of amino group in unfolded SPI molecules, forming a mesh structure. However, under alkaline conditions (pH 9), adhesive viscosity and stability increased compared to the original pH. This shift was due to the disruption of the SPI colloidal charge structure, an increase in the stretching of functional groups, further unfolding of the structure, and an enhanced binding of SPI to TA. Under the initial pH conditions, SPI reacted with TA's active site to form covalent crosslinked networks and hydrogen bonds. In alkaline condition, beyond hydrogen and ionic bonding, the catechol structure was oxidized, forming an ortho-quinone that crosslinked SPI and created a denser structure. Tensile strength measurements and freeze-thaw experiments revealed that the adhesive exhibited maximum tensile strength and optimal adhesion with 0.75% TA at pH 9, providing the best overall performance. This study provides a new formulation and approach for developing plant-based meat analogues adhesives.

Synthetic Polypeptide Bioadhesive Based on Cation-π Interaction and Secondary Structure.

Bioadhesives have garnered widespread attention in the biomedical field, for wound healing and tissue sealing. However, challenges exist due to the inferior performance of bioadhesives, including weak adhesion, poor biocompatibility, or lack of biodegradability. In this work, we demonstrate the fabrication of hydrogel adhesive based on polypeptides composed of lysine and glutamic acid. The cation-π interaction between the ammonium cations and phenyl groups endows the hydrogel with strong cohesion, and the hydrophobicity of the phenyl group significantly enhances the interaction between polypeptides and the substrate interface, leading to excellent adhesive performance. The equivalent molar ratio of ammonium cations and the phenyl group is beneficial for the enhancement of adhesiveness. Furthermore, we discover that the polypeptides with an α-helix exhibit better adhesiveness than the polypeptides with a ß-sheet because the α-helical structure can increase the exposure of the side group on the polypeptide surface, which further strengthens the interaction between polypeptides and the substrate. Besides, this synthetic polypeptide adhesive can seal the tissue quickly and remain intact in water. This adhesive holds significant promise for application in wound healing and tissue sealing, and this study provides insight into the development of more peptide-based adhesives.

Preparation of tannic acid-reinforced cellulose nanofiber composites for all-water-based high-performance wood adhesives.

Traditional adhesives easily release toxic gases during the preparation process or apply to wood composite products, which have adverse effects on the human body and the environment. Herein, an all-water-based high-performance wood adhesive is prepared using TEMPO-oxidized cellulose nanofiber (TOCNF), acrylamide (AM), and tannic acid (TA) through free radical polymerization. Different characteristics of the prepared composites, including morphology, injectability, and adhesion properties, have been investigated. Results showed that the TA/TOCNF/PAM composite has excellent injectability. The addition of TA can enhance the lap shear strength of the TA/TOCNF/PAM composites and with the increment of TA content, the lap shear strength gradually decreases. The formation of effective hydrogen bonds and Van der Waals interaction among the rich functional groups in the composite, lead to strong lap shear strength on different substrates. The composite with 5.0 g of AM, 5.0 g of the TOCNF suspension and 0.1 g TA possesses a high lap shear strength of 10.5 MPa on wood and 1.5 MPa on aluminium. Based on strong adhesion properties and excellent injectability, the TA/TOCNF/PAM composites have great potential in the furniture construction and building industries.

Amination and crosslinking of acetone-fractionated hardwood kraft lignin using different amines and aldehydes for sustainable bio-based wood adhesives.

Hardwood kraft lignin from the pulping industry is burned or discarded. Its valorization was conducted by subjecting fractionation, amination with ethylenediamine, diethylenetriamine, and monoethanolamine, and crosslinking with formaldehyde or glyoxal to obtain bio-based wood adhesives. Acetone-soluble and insoluble hardwood kraft lignin were prepared and subjected to amination and then crosslinking. Fourier transform infrared, 13C NMR, 15N NMR, and X-ray photoelectron spectroscopy results revealed successful amination with amide, imine, and ether bonds and crosslinking of all samples. Hardwood kraft lignin aminated with diethylenetriamine/ethylenediamine and crosslinked using glyoxal exhibited excellent results in comparison with samples crosslinked using formaldehyde. Acetone-insoluble hardwood kraft lignin aminated and crosslinked using diethylenetriamine and formaldehyde, respectively, exhibited excellent adhesion strength with plywood, satisfying the requirements of the Korean standards. The amination and crosslinking of industrial waste hardwood kraft lignin constitute a beneficial valorization method.

Tyrosinase-Modified UHMW SELP Polymers as Wet and Underwater Adhesives to Achieve Multi-interface Adhesion.

The presence of a hydration layer in humid and underwater environments challenges adhesive-substrate interactions and prevents effective bonding, which has become a significant obstacle to the development of adhesives in the industrial and biomedical fields. In this study, ultrahigh-molecular-weight (UHMW) silk-elastin-like proteins (SELP) with 3,4-dihydroxyphenylalanine (DOPA) converted from tyrosine residues by tyrosinase exhibited excellent adhesive properties on different interfaces, such as glass, aluminum, wood, polypropylene sheets, and pigskin, under both dry and wet conditions. Additionally, by incorporating trace amounts of cross-linking agents like Fe3+, NaIO4, and tris(hydroxymethyl) phosphine (THP), the mussel-inspired adhesives maintained a stable and excellent adhesion, broadening the conditions of application. Notably, the UHMW SELP adhesive exhibited remarkable underwater adhesion properties with a shear strength of 0.83 ± 0.17 MPa on glass. It also demonstrated good adhesion to biological tissues including the kidney, liver, heart, and lungs. In vitro cytocompatibility testing using L929 cells showed minimal toxicity, highlighting its potential application in the biomedical field. The sustainable, cytocompatible, cost-effective, and highly efficient adhesive provides valuable insights for the design and development of a new protein-based underwater adhesive for medical application.

A polyethylene glycol-grafted pullulan polysaccharide adhesive improves drug loading capacity and release efficiency.

In this study, polyethylene glycol was grafted onto pullulan polysaccharides, resulting in the development of a novel adhesive termed PLUPE, offering superior drug loading capacity and rapid release efficiency. The efficacy of PLUPE was rigorously evaluated through various tests, including the tack test, shear strength test, 180° peel strength test, and human skin adhesion test. The results demonstrated that PLUPE exhibited a static shear strength that was 4.6 to 9.3 times higher than conventional PSAs, ensuring secure adhesion for over 3 days on human skin. A comprehensive analysis, encompassing electrical potential evaluation, calculation of interaction parameters, and FT-IR spectra, elucidated why improved the miscibility between the drug and PSAs, that the significant enhancement of intermolecular hydrogen bonding in the PLUPE structure. ATR-FTIR, rheological, and thermodynamic analyses further revealed that the hydrogen bonding network in PLUPE primarily interacted with polar groups in the skin. This interaction augmented the fluidity and free volume of PSA molecules, thereby promoting efficient drug release. The results confirmed the safety profile of PLUPE through skin irritation tests and MTT assays, bolstering its viability for application in TDDS patches. In conclusion, PLUPE represented a groundbreaking adhesive solution for TDDS patches, successfully overcoming longstanding challenges associated with PSAs.

Rhamnose-PEG-induced supramolecular helices: Addressing challenges of drug solubility and release efficiency in transdermal patch.

Transdermal drug delivery systems (TDDS) demand both high drug loading capacity and efficient delivery. In order to improve both simultaneously, this study aims to develop a novel rhamnose-induced pressure-sensitive adhesive (HPR) by dispersing the drug in the supramolecular helical structure. Ten model drugs, categorized as acidic and basic compounds, were chosen to understand the characteristics of the HPR and its inner mechanism. Notably, it enhanced drug loading by 1.41 to 5 times over commercially available pressure-sensitive adhesives Duro-Tak@ 87-4098 and Duro-Tak@ 87-2287, in addition to increasing drug release efficiency by a factor of about 5. Pharmacokinetic evaluation demonstrated that the HPR group had >4-fold (Tulobuterol TUL) and 3-fold (Diclofenac DIC) more area under the blood drug concentration curve (AUC) than the commercial TUL and DIC patches in the absence of added excipients and a significantly prolonged mean residence time (MRT) of >4-fold (TUL) and 3-fold (DIC), demonstrating the potential for highly efficacious and prolonged dosing. Furthermore, its safety and mechanical properties meet the requisite standards. Mechanistic inquiries unveiled that both acidic and basic drugs establish hydrogen bonds with HPR and become encapsulated within supramolecular helical structures. The supramolecular helical structures, significantly elevated both the enthalpy of the drug-HPR and entropy of the drugs release, thereby substantially enhancing drug delivery efficiency. In summary, HPR enabled a significant simultaneous enhancement of drug loading and drug delivery, which, together with its unique spatial structure, would contribute to the development of TDDS. In addition, the establishment of rhamnose-induced supramolecular helical structures would provide innovative pathways for different drug delivery systems.

Lobster-Inspired Chitosan-Derived Adhesives with a Biomimetic Design.

Polysaccharide-based adhesives, especially chitosan (CS)-derived adhesives, serve as promising sustainable alternatives to traditional adhesives. However, most demonstrate a poor adhesive strength. Inspired by the inherent layered structure of marine arthropods (lobsters), a core-shell structure (SiO2-NH2@OPG) with amine-functionalized silica (SiO2-NH2) as the core and oxidized pyrogallol (OPG) as the shell is prepared in this study. The compound is blended with CS to produce a structural biomimetic wood adhesive (SiO2-NH2@OPG/CS) with excellent performance. In addition to thermocompressive curing, this adhesive exhibits a water-evaporation-induced curing behavior at room temperature. With reference to the design mechanism of the lobster cuticle, this microphase-separated structure consists of clustered nanofibers with varying amounts of SiO2-NH2@OPG particles between the fibers. This intriguing microphase structure and its mechanical effects could offer a powerful solution for improving the functional modification of wood composites.

Bioinspired Injectable Polyurethane Underwater Adhesive with Fast Bonding and Hemostatic Properties.

Underwater adhesives with injectable, organic solvent-free, strong, fast adhesion, and hemostatic properties have become an urgent need in biomedical field. Herein, a novel polyurethane underwater adhesive (PUWA) inspired by mussels is developed utilizing the rapid post-cure reaction of isocyanate esterification without organic solvents. The PUWA is created through the injectable two component curing process of component A (biocompatible polyurethane prepolymer) and component B (dopamine modified lysine derivatives: chain extender-LDA and crosslinker-L3DA). The two-component adhesive cures quickly and firmly underwater, with an impressive bonding strength of 40 kPa on pork skin and excellent burst pressure of 394 mmHg. Moreover, the PUWA exhibits robust adhesion strength in hostile environments with acid, alkali and saline solutions. Combined with excellent biocompatibility and hemostatic performance, the PUWA demonstrates effectively sealing wounds and promoting healing. With the ability to bond diverse substrates rapidly and strongly, the PUWA holds significant potential for application in both biomedical and industrial fields.

Magneto-Induced Janus Adhesive-Tough Hydrogels for Wearable Human Motion Sensing and Enhanced Low-Grade Heat Harvesting.

Janus hydrogels with different properties on the two surfaces have considerable potential in the field of material engineering applications. Various Janus hydrogels have been developed, but there are still some problems, such as stress mismatch caused by the double-layer structure and Janus failure caused by material diffusion in the gradient structure. Here, we report a Janus adhesive-tough hydrogel with polydopamine-decorated Fe3O4 nanoparticles (Fe3O4@PDA) at one side induced by magnetic field to avoid uncontrollable material diffusion in the cross-linking polymerization of acrylamide with alginate-calcium. The magneto-induced Janus (MIJ) hydrogel has an adhesive surface and a tough bulk without an obvious interface to avoid stress mismatch. Due to the intrinsic dissipative matrix and the abundant catechol groups on the adhesive surface, it shows strong adhesion onto various substrates. The MIJ hydrogel has high sensitivity (GF = 0.842) in detecting tiny human motion. Owing to the synergy of Fe3O4@PDA-enhanced interfacial adhesion and heat transfer, it is possible to quickly generate effective temperature differences when adhering to human skin. The MIJ hydrogel achieves a Seebeck coefficient of 13.01 mV·K-1 and an output power of 462.02 mW·m-2 at a 20 K temperature difference. This work proposes a novel strategy to construct Janus hydrogels for flexible wearable devices in human motion sensing and low-grade heat harvesting.

A Rhamnose-PEG-Modified Dendritic Polymer for Long-Term Efficient Transdermal Drug Delivery.

This study introduces a dendronized pressure-sensitive adhesive, TMPE@Rha, addressing Food and Drug Administration (FDA) concerns about traditional pressure-sensitive adhesives (PSAs) in transdermal drug delivery systems. The unique formulation, composed of rhamnose, trihydroxypropane, and poly(ethylene glycol), significantly enhances cohesion and tissue adhesion. Leveraging rhamnose improves intermolecular interactions and surface chain mobility, boosting tissue adhesion. Compared to acrylic pressure-sensitive adhesive 87-DT-4098, TMPE@Rha shows substantial advantages, with up to 5 to 6 times higher peel strength on porcine and wood substrates. Importantly, it maintains strong human skin adhesion beyond 7 days without the typical "dark ring" phenomenon. When loaded with diclofenac, the adhesive exhibits 3.12 times greater peeling strength than commercial alternatives, sustaining human adhesion for up to 6 days. Rigorous analyses confirm rhamnose's role in increasing interaction strength. In vitro studies and microscopy demonstrate the polymer's ability to enhance drug loading and distribution on the skin, improving permeability. Biocompatibility tests affirm TMPE@Rha as nonirritating. In summary, TMPE@Rha establishes a new standard for PSAs in transdermal drug delivery systems, offering exceptional adhesion, robustness, and biocompatibility. This pioneering work provides a blueprint for next-generation, highly adhesive, drug-loaded PSAs that meet and exceed FDA criteria.

A nature-inspired multifunctional adhesive for cartilage tissue-biomaterial integration.

Surgical adhesives play a crucial role in tissue integration and repair, yet their application in wet conditions has been severely limited by inadequate adhesive strength and subpar biocompatibility. Furthermore, tissue adhesives have rarely been reported in cartilage tissue repair. In this study, a three-armed dopamine-modified hyaluronic acid derivative adhesive was prepared to function as a bio-inspired adhesive in moist environments. To meet the clinical requirements for cartilage tissue adhesion, we studied its chemical structure, including microscopic morphology, adhesion properties with materials and tissues, in vivo degradation rules, and biological evaluation. The OGMHA8-DOPA adhesive with the optimal aldehyde substitution degree and dopamine-grafting rate was determined by analyzing the experimental conditions. SEM results revealed that the cartilage tissue adhered to a porous interconnected structure. The excellent biocompatibility of the material not only facilitated chondrocyte adhesion but also supported their proliferation on its surface. Animal experiments have demonstrated that this material has no observable inflammatory response or incidence of fibrous capsule formation. The degradation timeline of the material extends beyond the duration of two weeks. The dopamine-modified adhesive exhibited a tight interfacial binding force between the biomaterial and cartilage tissue and excellent biocompatibility in watery tissue, revealing its potential for application in cartilage tissue repair and minimally invasive surgery.

Instant tough adhesion of polymer networks.

Generating strong rapid adhesion between hydrogels has the potential to advance the capabilities of modern medicine and surgery. Current hydrogel adhesion technologies rely primarily on liquid-based diffusion mechanisms and the formation of covalent bonds, requiring prolonged time to generate adhesion. Here, we present a simple and versatile strategy using dry chitosan polymer films to generate instant adhesion between hydrogel-hydrogel and hydrogel-elastomer surfaces. Using this approach we can achieve extremely high adhesive energies (>3,000 J/m2), which are governed by pH change and non-covalent interactions including H-bonding, Van der Waals forces, and bridging polymer entanglement. Potential examples of biomedical applications are presented, including local tissue cooling, vascular sealing, prevention of surgical adhesions, and prevention of hydrogel dehydration. We expect these findings and the simplicity of this approach to have broad implications for adhesion strategies and hydrogel design.

Black phosphorus boosts wet-tissue adhesion of composite patches by enhancing water absorption and mechanical properties.

Wet-tissue adhesives have long been attractive materials for realizing complicated biomedical functions. However, the hydration film on wet tissues can generate a boundary, forming hydrogen bonds with the adhesives that weaken adhesive strength. Introducing black phosphorus (BP) is believed to enhance the water absorption capacity of tape-type adhesives and effectively eliminate hydration layers between the tissue and adhesive. This study reports a composite patch integrated with BP nanosheets (CPB) for wet-tissue adhesion. The patch's improved water absorption and mechanical properties ensure its immediate and robust adhesion to wet tissues. Various bioapplications of CPB are demonstrated, such as rapid hemostasis (within ~1-2 seconds), monitoring of physical-activity and prevention of tumour-recurrence, all validated via in vivo studies. Given the good practicability, histocompatibility and biodegradability of CPB, the proposed patches hold significant promise for a wide range of biomedical applications.

Preparation and structural characterization of epoxidized soybean oils-based pressure sensitive adhesive grafted with tea polyphenol palmitate.

Vegetable oils-based pressure sensitive adhesives (PSAs) are green and sustainable but face unsatisfactory adhesion strengths and are prone to aging during storage and application due to the existence of residual double bonds and massive ester bonds. Nine common antioxidants (tea polyphenol palmitate (TPP), caffeic acid, ferulic acid, gallic acid, butylated hydroxytoluene, tertiary butylhydroquinone, butylated hydroxyanisole, propyl gallate, and tea polyphenols) were grafted into epoxidized soybean oils-PSA (ESO-PSA) system to enhance antiaging properties and adhesion strengths. Results showed ESO-PSAs grafted with caffeic acid, tertiary butylhydroquinone, butylated hydroxyanisole, propyl gallate, tea polyphenols, or TPP didn't occur failure with TPP having best performance. The optimal conditions were ESO reacted with 0.9 % TPP, 70 % rosin ester, and 7.0 % phosphoric acid at 50 °C for 5 min, under which peel strength and loop tack increased to 2.460 N/cm and 1.66 N, respectively, but peel strength residue reduced to 138.09 %, compared with control (0.407 N/cm, 0.43 N, and 1669.99 %). Differential scanning calorimetry and thermogravimetric results showed TPP grafting increased the glass transition temperature of ESO-PSA slightly but improved its thermal stability significantly. Fourier transform infrared spectroscopy and 1H nuclear magnetic resonance results showed TPP, phosphoric acid, and rosin ester all partially participated in the covalently crosslinking polymerization of ESO-PSAs and the rest existed in the network structures in the free form.

Synthesis and characterization of a bio-aldehyde-based lignin adhesive with desirable water resistance.

Wood-based panels find widespread application in the furniture and construction industries. However, over 90 % of adhesives used are synthesized with formaldehyde, leading to formaldehyde emission and associated health risks. In this study, an entirely bio-based adhesive (OSL) was innovatively proposed through the condensation of multi-aldehyde derived from the oxidization of sucrose (OS) with sodium lignosulfonate (L). This approach positioned oxidized sucrose (OS) as a viable substitute for formaldehyde, ensuring safety, simplicity, and enhance water resistance upon reaction with L. The optimization of the OSL adhesive preparation process involved determining the oxidant level for high sucrose conversion to aldehyde (13 % based on sucrose), the mass ratio of OS to L (0.8), and hot-pressing temperature (200 °C). Notably, the shear strength of 3-plywood bonded with the developed adhesive (1.04 MPa) increased to 1.42 MPa after being immersed in hot water at 63 ±â€¯3 °C for 3 h. Additionally, the plywood specimens exhibited excellent performance after soaking in boiling water for 3 h, resulting in a shear strength of 1.03 MPa. Chemical analysis using Fourier-transform infrared spectroscopy (FTIR), 1H nuclear magnetic resonance (NMR), and X-ray photoelectron spectroscopy (XPS) confirmed an addition reaction between L and OS, forming a dense network structure, effectively enhanceing the water resistance of OSL adhesives. Furthermore, compared with lignin-formaldehyde resin adhesive (LF), the OSL adhesive exhibited superior wet shear strength. This study offered an innovative approach for developing lignin-based adhesives utilizing a biomass aldehyde (OS), as a promising substitute for formaldehyde in the wood industry. The findings indicated that this approach may advance lignin-based adhesives, ensuring resistance to strength deterioration under highly humid environmental conditions.

Bonding performance and surface characterization of cold-bonded acetylated beech (Fagus sylvatica L.) laminated veneer lumber.

Acetylation of wood with acetic anhydride reduces the wood-moisture interaction, improves the dimensional stability and resistance against biodegradation. However, the adhesive bonding is affected by the modification, which is crucial to manufacture engineered wood products, such as laminated veneer lumber (LVL). In this study we report the bonding of 8-layered acetylated beech (Fagus sylvatica L.) LVL boards to 2-layered LVL beams. The beams were glued together at room temperature adding three common load-bearing construction adhesives: melamine-urea-formaldehyde (MUF), phenol-resorcinol-formaldehyde (PRF), and one-component polyurethane (PUR). The bonding performance was tested by assessing its dry and wet tensile shear strength (TSS) and wood failure percentage (WF). Also evaluated were the material's density and moisture content (MC). The surface was characterized prior to bonding by its pH, roughness, and contact angle (CA). The adhesive penetration was observed by fluorescence microscopy. Aside from MUF, applying PRF and PUR adhesives achieved good bonding performance on acetylated LVL and references. Acetylated LVL displayed a more hydrophobic behaviour, a higher pH, a somewhat smoother surface, and an increased density.

Pulp cellulose-based core-sheath structure based on hyperbranched grafting strategy for development of reinforced soybean adhesive.

Formaldehyde adhesive is the primary source of indoor formaldehyde pollution, posing a serious threat to human health. Soybean meal (SM), as an abundant biomacromolecule and co-product of soybean oil industry, emerges as a promising alternative to formaldehyde adhesive. However, the SM adhesive exhibits inferior water resistance and unsatisfactory bonding strength. In this study, a novel core-sheath structure with an inexpensive pulp cellulose core and a hyperbranched polymer sheath is synthesized and introduced into SM to develop a robust bio-based adhesive. Specifically, aldehyde-functionalized pulp cellulose is grafted with hyperbranched polyamide, which is terminated via epoxy groups, to synthesize a core-sheath hybrid (APC@HBPA-EP). The core-sheath APC@HBPA-EP serves as both a crosslinker and an enhancer. The results show that the wet shear strength of the modified SM adhesive exhibits a remarkable 520 % increase to 0.93 MPa, and its dry shear strength reaches 2.10 MPa, meeting the established indoor use standards. The Young's modulus of the modified SM adhesive shows a significant 282 % increase to 19.27 GPa. Additionally, the modified SM adhesive exhibited superior impact toughness (7.48 KJ/m2), which increased by 24 times compared with pure SM adhesive. This study provides a versatile strategy for developing robust protein adhesives, hydrogel patch, and composite coatings.

Preparation of reed fibers reinforced graft-modified starch-based adhesives based on quantum mechanical simulation and molecular dynamics simulation.

Starch is a biomass polymer material with a high yield and comprehensive source. It is used as a raw material for preparing adhesives because of its highly active hydroxyl group. However, poor adhesion and water resistance hinder the application of starch-based adhesives (SBAs). Based on this, the starch was modified through graft copolymerization with itaconic acid as a cross-linking agent, methyl methacrylate and methyl acrylate as copolymers. Additionally, reed fibers were synergistically modified with polydopamine deposition to prepare an environmentally friendly SBA used in plywood production. Fourier transform infrared spectroscopy (FT-IR), nuclear magnetic resonance spectroscopy (1H NMR), X-ray diffraction (XRD), and thermogravimetric analysis (TG) demonstrate that copolymerization of methyl methacrylate and methyl acrylate with starch improves the shear strength, water resistance, and thermal stability of the SBA. Compared to unmodified starch, the modified SBA exhibits a 129 % increase in dry strength and achieves a wet strength of 1.36 MPa. Fukui function, Frontier orbit theory, and molecular dynamics simulation have shown that itaconic acid promotes the copolymerization of starch and acrylate monomers. The modified starch has fewer hydrogen bonds, less order, and a denser macromolecular network structure, which provides a reference for studying the molecular interaction mechanisms of SBAs.